8.4 大量 成型脱模 ( Massive forming )


BECHEM 潤滑油 Bechem 冷锻型油 Beruform 系列。

BECHEM 大量 成型脱模产品包含 BerulitBeruforge 两大类产品


产品 加工/应用 特性
Beruforge 100
含二硫化钼 ( MoS2) 润滑涂层,特种添加剂允许形成无磷化层 ( Coating lubricant containing MoS2, special additives allow forming without phosphate layer)
Beruforge 120 D
含有蜡涂层的冷锻大规模成型剂,含特殊添加剂,因此具备优异的压力稳定性 ( Wax containing coating lubricant for cold massive forming, excellent pressure stability based on special additives )
Beruforge 170
含有二硫化钼(Mos2) 的涂层润滑剂,具有极小的颗粒尺寸,因此成型件可获得极佳的表面特性 ( MoS2 containing coating lubricant with a low particle size, thus excellent surface qualities are achieved )
Berulit 913
半热锻用涂层润滑剂,可防止成型件表面产生鳞状,具高温稳定性,采用特殊添加剂,因此也非常适合于钢或铝的热轧成型 ( Coating lubricant for semi-hot forging, prevents scaling on the surface, high temperature stability, based on special additives also highly suitable for hot and profile rolling of steel and aluminium )
Berulit 935
半热锻用涂层润滑剂,可防止成型件表面产生鳞状,具高温稳定性,工具温度可介于 120 °C 至 380 °C 之间 ( Coating lubricant for semi-hot forging, prevents scaling on the surface, high temperature stability, tool temperatures from +120 °C to +380 °C )
Beruforge 182
涂层润滑剂,可防止鳞状表面的形成至温度1280℃,并防止炉内溶接 ( Coating lubricant which prevents scale formation up to +1.280 °C and welding of the parts in the furnace )
Beruforge 2002 B
钢与非铁类金属热轧用的润滑剂,非常适合于半热锻工艺所常采用的循环式冷却润滑,模具温度为140°C至+300℃之间 ( Graphite-free lubricant for hot and profile rolling of steel and nonferrous metals, in addition highly suitable for circulation cooling and lubrication in semi-hot forging processes, tool temperatures from +140 °C to +300 °C )
Berulit 912 HP
一般半热锻成型所采用的循环式冷却润滑剂,模具温度为120°C至+300℃之间 ( Universal lubricant for circulation cooling and lubrication in semi-hot forging processes, tool temperatures from +120 °C to +350 °C )
Beruforge 393 G
铝,镁金属用具有低石墨含量及蜡质的润滑剂,工具温度介于120℃至300℃之间 ( Lubricant with a low graphite content and waxy additives for forming of aluminium and magnesium, tool temperatures from +120 °C to +300 °C )
Berulit 740-88
适于钢或黄铜合金等的模锻或热锻,尤其是组件为中空的型式 ( Suitable for die forging and hot forging of steel and brass alloys, especially for the production of hollow parts )
Berulit 906 HP
含有石墨且具有极小颗粒尺寸的润滑剂,适用于极度要求的模锻制程,工具温度介于120℃至350℃之间 ( Graphite containing lubricant with a low particle size for extreme requirements in die forging, tool temperatures from +120 °C to +350 °C )